The basic principles of metal surface treatment agent to solve the adhesion of metal

Hits:Updated:2016-08-04 14:08:41【Print】

   Most real fresh metal surface has a higher surface free energy (500 ~ 5000mN / m), far higher than the surface of the organic polymer material can (less than 100mN / m). This high energy surface adhesion of the coating is very advantageous, in fact, a lot of metal in the air is easy to produce an oxide film, the surface free energy is relatively lower, affect the paint adhesion, but in any case, the vast majority of the surface of a metal oxide film still higher than the free energy of a conventional light-cured coatings, paint and therefore not a big problem for the metal substrate wetting should. However, UV coating applied to metal substrates often encountered problem is poor adhesion to the metal coating, if no special features to add additives, conventional UV coating for metal is difficult to obtain a good adhesion, which may because dense metal substrate surface, the organic coating can not penetrate absorption, the less significant the contact interface, unlike paper, plastic, wood and other substrates can be formed as penetration anchor structure. Another reason may be the most acrylic ester resin and a higher cure shrinkage monomers have a relationship, the internal stress generated by curing shrinkage of the film is largely a reaction to the metal substrate adhesion. Metal blasting, phosphate, electrochemical treatment, may help to improve coating adhesion, but after all, is only one aspect relating to adhesion problems, and these treatments exist or affect the appearance or reduce the coating efficiency and other issues. How to adjust the formula to improve the photo-curable coating adhesion on various metal substrates UV industry is more concerned about the issue.
  Solve coating adhesion solution is often to add an adhesion promoter in UV coating formulations, the source Accor chemical treatment agents used in metal enhance the adhesion of UV metal, from a connecting role, hinges on the substrate and UV, to achieve adhesion . Widely used in all kinds of zinc alloy, magnesium alloy, stainless steel hardware and water on the vacuum coating or plating, can assist in strengthening the bonding metal layer and UV coating, while the most commonly used solvent and has a good affinity resin, widely recognized by the market is a common type of treatment agent.
  Physical properties:
  1. Appearance: light yellow turbid liquid
  2, solid content: 25%
  3, softening temperature: about 80 ℃
  4, molecular weight: 60000-90000
  Construction Technology:
  1, the cleaning → spraying metal coating process hardware (PVD) coating the surface of the treated water for 3-5 minutes to dry → → → IR UV paint spraying leveling (60 ± 10 ℃ × 4 ~ 6min) → UV curing (700 ± 100mj / cm2) → test, the next step.
  2, the application viscosity: 8 ± 1 seconds (Iwata Cup # 2)
  3, working pressure: 3-4Kg / cm2
  4, coating film thickness: thickness of the coating metal treatment agent is generally controlled between 3-5μm best effect, UV paint film thickness is 10-15μm
  

Previous:

Poor adhesion of metal spray solution

Next:

  No Close
Share:
客服中心
工作時(shí)間

周一至周日

8:00 - 18:00

點(diǎn)擊這里給我發(fā)消息 銷售客服


請直接QQ聯(lián)系!
展開客服
宁蒗| 玉田县| 乐安县| 岢岚县| 溧水县| 略阳县| 保定市| 黔西县| 房产| 英德市| 宜君县| 衡阳市| 剑阁县| 潼南县| 铜梁县| 中牟县| 隆林| 土默特右旗| 垦利县| 阜城县| 莲花县| 锡林郭勒盟| 博兴县| 伊金霍洛旗| 临汾市| 鄂托克旗| 田东县| 武冈市| 黑龙江省| 绥宁县| 衡阳县| 涟水县| 辽中县| 乌鲁木齐市| 赫章县| 集安市| 黄龙县| 青龙| 大余县| 香河县| 万安县|